Glavni vzrok površinske poškodbe aluminijastih profilov
1. Na površino ingota ali segregacije sestave ingot so pritrjene nečistoče. When there is a large number of segregation floats on the surface of the ingot and the ingot is not homogenized or the homogenization effect is not good, there are a certain number of hard metal particles in the ingot, and when the metal flows through the working belt during the extrusion process, these segregation floats or hard metal particles attach to the surface of the working belt or cause damage to the working belt, and finally cause scratches to the surface of the profile;
2. Na plesni votlini ali delovnem pasu obstajajo raznolike, trdota delovnega pasu plesni pa je nizka, tako da je površina delovnega pasu poškodovana in ob ekstrudiranju opraska profil.
3. V grafitnem traku so izpostavljeni kovinski ali trdi vključki na praznjenju ali nihalu, kar bo povzročilo praske na površini profila, ko pride v stik s profilom;
4. Ko palica za vilice pošlje profil s proge, ki se odvaja na nihajoča postelja, se profil poškoduje zaradi prekomerne hitrosti;
5. Umetno vlečenje profila na postelji povzroča odrgnine;
6. Med prevozom se profili drgnejo drug proti drugemu ali stisnejo drug drugega, da povzročijo škodo
Rešitev
1. okrepiti nadzor kakovosti ingot;
2. izboljšati kakovost popravila plesni, redno nitriranje plesni in strogo izvajanje nitridiranja;
3. Za izolacijo profila iz pomožne naprave uporabite Soft Felt, da zmanjšate poškodbo stika med profilom in pomožno napravo;
4. V proizvodnji je treba ravnati previdno in se poskušati izogniti vlečenju ali obračanju profila po volji;
5. Profile postavite razumno v okvir materiala in se poskusite izogniti trenju med seboj.