1. The quality of heat treatment of aluminum extrusion die directly affects the service life of the extrusion die. Quenching is to improve the hardness of the mold, and repeated tempering is to improve the toughness of the mold and stabilize the internal structure. The hardness value of mold heat treatment is specified: large aluminum extrusion die (F>500 mm), HRC45-48; Srednja plesen (F300 ~ 500 mm), HRC47-50; Majhna ekstruzijska matrica (F<300mm), HRC48-51; Three points are tested on the same plane of a set of molds, and the hardness value of each point should be qualified within the specified range.
2. Posebno pozornost je treba nameniti več točkam v postopku toplotne obdelave ekstruzije:
a. Hitrost ogrevanja temperaturnega odseka visoke - mora biti hitra, čas zadrževanja pa ne bi smel biti predolg, da bi preprečili, da bi se ekstruzijska matrica zaradi pregrevanja ali pregrevanja pregrela - groba zrna, pregrevanje - nizke taljene točke, ki bodo povzročili pregrevanje;
b. Po gašenju je treba aluminijasto ekstruzijo umreti pravočasno ublažiti, da se prepreči razpoke;
c. Kadar se ugotovi, da je trdota ekstruzijske matrice po toplotni obdelavi nezadostna ali neenakomerna, je treba izvesti žarjenje in toplotno obdelavo - izvesti v skladu s postopkom (kadar je vrednost trdote
d. Za velike aluminijeve ekstruzijske kalupe ali končne kalupe s kompleksnimi votlinami je treba dodati stres - razbremenitev kaljenja (za odpravljanje električne obdelave in obdelave stresa, to je za odpravo toplotnega stresa in mikrostrukturnega napetosti);
e. Temperatura gašenja olja kalupa mora biti 100 stopinj, da se zagotovi učinek gašenja.